موليبډينوم

موليبډينوم (په انگرېزي: Molybdenum) له کیمیاوي عناصرو څخه یو دی چې په تناوبي جدول کې د Mo سمبول او ۴۲ اتمي شمېرې په وسیله ښودل شوی دی.

Molybdenum,  ₄₂Mo

عمومي خواص
Pronunciation	/ˌmɒlɪbˈdiːnəm/ or /məˈlɪbdɪnəm/ MOL-ib-DEE-nəm or MƏ-LIB-DIN-əm
Appearance	gray metallic
Molybdenum په دوراني جدول کې
Cr ↑ Mo ↓ W niobium ← molybdenum → technetium ‍
اټومي شمیره (Z)	42
گروپ, پیریود	group 6, period 5
بلاک	d-block
Element category	transition metal
معياري اټومي وزن (Ar)	کينډۍ:Val[۱]
Electron configuration	[Kr] 4d5 5s1
Electrons per shell	2, 8, 18, 13, 1
فزیکي خواص
حالت (at STP)	جامد
دويلې کيدو ټکى	2896 K ​(2623 °C, ​4753 °F)
يشنا ټکی	4912 K ​(4639 °C, ​8382 °F)
Density near r.t.	10.28 g/cm3
when liquid, at m.p.	9.33 g/cm3
Heat of fusion	37.48 kJ/mol
Heat of vaporization	598 kJ/mol
Molar heat capacity	24.06 J/(mol·K)
Vapor pressure P (Pa) 1 10 100 1 k 10 k 100 k at T (K) 2742 2994 3312 3707 4212 4879
اټومي خواص
Oxidation states	6, 5, 4, 3, 2, 1,[۲] −1, −2, −4 ​(a strongly acidic oxide)
Electronegativity	Pauling scale: 2.16
Ionization energies	1st: 684.3 kJ/mol 2nd: 1560 kJ/mol 3rd: 2618 kJ/mol
Atomic radius	empirical: 139 pm
Covalent radius	154±5 pm
Miscellanea
Crystal structure	​body-centered cubic (bcc)
Speed of sound thin rod	5400 m/s (at r.t.)
Thermal expansion	4.8 µm/(m·K) (at 25 °C)
د تودوخې تېرېدنه	138 W/(m·K)
Thermal diffusivity	54.3 mm2/s (at 300 K)[۳]
Electrical resistivity	53.4 nΩ·m (at 20 °C)
Magnetic ordering	paramagnetic[۴]
Magnetic susceptibility (χmol)	+89.0·10−6 cm3/mol (298 K)[۵]
Young's modulus	329 GPa
Shear modulus	126 GPa
Bulk modulus	230 GPa
Poisson ratio	0.31
Mohs hardness	5.5
Vickers hardness	1400–2740 MPa
Brinell hardness	1370–2500 MPa
CAS Number	7439-98-7
History
Discovery	Carl Wilhelm Scheele (1778)
First isolation	Peter Jacob Hjelm (1781)
Main isotopes of molybdenum
آيسو­ټوپ Abun­dance نیم ژوند (t1/2) Decay mode Pro­duct 92Mo 14.65% stable 93Mo syn 4×103 y ε 93Nb 94Mo 9.19% stable 95Mo 15.87% stable 96Mo 16.67% stable 97Mo 9.58% stable 98Mo 24.29% stable کينډۍ:Infobox element/isotopes decay2 100Mo 9.74% 7.8×1018 y β−β− 100Ru
view • talk • edit | references | in Wikidata